Etching problem
![]()
2016/6/9 8:10:46
There are two PCBs goes to the etching process, and on
two separate occasions each with new Ferric Chloride
mixture, a discolourment will occur and the PCB will
turn a tint black, then after a while it turns green, or drys to a dark brown. What is going wrong?
Mikael
2016/11/25 21:41:30
Warming FeCl will speed the process a lot, and give it less time to go wrong. Of course, it also goes faster to be wrong.
James
2016/10/20 12:13:25
Th eprocess you are doing is exposing the PCB's to the UV light, it should not take more than about 15 mins. So I guess the problem maybe because you are exposed too long.
Dan
2016/9/27 11:09:05
It depends on the temperature of your ferric solution. The best should be around 100F. The water you used will also effect the result. Distilled water will give better results than tap water.
Adair
2016/6/11 8:10:46